| 牌號 | 化學成分/% | |||||||
| Si | Al | Ca | Mn | Cr | P | S | C | |
| 范圍 | ≤ | |||||||
| FeSi75A10.5-A | 74.0-80.0 | 0.5 | 1 | 0.4 | 0.3 | 0.035 | 0.02 | 0.1 |
| FeSi75A10.5-B | 72.0-80.0 | 0.5 | 1 | 0.5 | 0.5 | 0.04 | 0.02 | 0.2 |
| FeSi75A11.0-A | 74.0-80.0 | 1 | 1 | 0.4 | 0.3 | 0.035 | 0.02 | 0.1 |
| FeSi75A11.0-B | 72.0-80.0 | 1 | 1 | 0.5 | 0.5 | 0.04 | 0.02 | 0.2 |
| FeSi75A11.5-A | 74.0-80.0 | 1.5 | 1 | 0.4 | 0.3 | 0.035 | 0.02 | 0.1 |
| FeSi75A11.5-B | 72.0-80.0 | 1.5 | 1 | 0.5 | 0.5 | 0.04 | 0.02 | 0.2 |
| FeSi75A12.0-A | 74.0-80.0 | 2 | 1 | 0.4 | 0.3 | 0.035 | 0.02 | 0.1 |
| FeSi75A12.0-B | 74.0-80.0 | 2 | 1 | 0.4 | 0.3 | 0.04 | 0.02 | 0.1 |
| FeSi75A12.0-C | 72.0-80.0 | 2 | 0.5 | 0.5 | 0.04 | 0.02 | 0.2 | |
| FeSi75-A | 74.0-80.0 | 0.4 | 0.3 | 0.035 | 0.02 | 0.1 | ||
| FeSi75-B | 74.0-80.0 | 0.4 | 0.3 | 0.04 | 0.02 | 0.1 | ||
| FeSi75-C | 72.0-80.0 | 0.5 | 0.5 | 0.04 | 0.02 | 0.2 | ||
| FeSi65 | 65.0-<72.0 | 0.6 | 0.5 | 0.04 | 0.02 | |||
| FeSi45 | 40.0-47.0 | 0.7 | 0.5 | 0.04 | 0.02 | |||
我廠供應75% 72% 65% 45% 四種牌號的硅鐵
硅鐵在鋼工業、鑄造工業及其他工業生產中被廣泛應用。
硅鐵是煉鋼工業中必不可少的脫氧劑。炬鋼中，硅鐵用于沉淀脫氧和擴散脫氧。磚坯鐵還作為合金劑用于煉鋼中。鋼中添加一定數量的硅，能顯著提高鋼的強度、硬度和彈性，提高鋼的磁導率，降低變壓器鋼的磁滯損耗。
高硅硅鐵或硅質合金在鐵合金工業中用作生產低碳鐵合金的還原劑。硅鐵加入鑄鐵中可作球墨鑄鐵的孕育劑，且能阻止碳化物形成，促進石墨的析出和球化，改善鑄鐵性能。
此外，硅鐵粉在選礦工業中可作懸浮相使用，在焊條制造業中作焊條的涂料
在煉鋼工業中，每生產一噸鋼大約消耗3～5kg75%硅鐵。
熔點：75FeSi為1300℃